Best Used for:

• Jigs and fixtures requiring minimal deflection at elevated temperature like drill holder, air intake
• Cover-plates and enclosures like automotive and motorsport interior
• Fastenings, tools & couplings
• Strong and stiff prototypes

Compatible Printers:

LC Magna (Not suitable for UV 3D Printers)

Features:

• Heat Deflection Temperature 80 °C
• High impact strength
• Tough, Durable, and long lasting
• Simulating the strength and stiffness of ABS
• High definition and can hold fine details
• Smooth surface finish


Next >

Properties

Tensile Properties
Tensile Modulus*: 2100 MPa ASTM D638
Ultimate Tensile Strength*: 60 MPa ASTM D638
Elongation at break*: 14% ASTM D638

Flexural Properties
Flexural Strength*: 81 MPa ASTM D790
Flexural Modulus*: 2080 MPa ASTM D790

Impact Properties

Impact Strength Notched Izod*: 110 J/m ASTM D256

General Properties

Hardness*: 85 Shore D ASTM D2240
Heat Deflection Temperature*: 80°C ASTM D648
Water Absorption (Short Term): 1.06% ASTM D570
Viscosity: 480 cPs At 25°C Brookfield spindle 3
Density: 1.14 g/cm3
Storage: 10-50°C
Colours: Black, White, Smoky Quartz Translucent

*Mechanical properties stated based on fully cured material.

Dimensions: 190 x 140 x 260mm


Next >

Processing Instructions

• To print with Photocentric Liquid Crystal Magna, choose ‘Durable DL110HB’ or ‘Durable DL110HW’ or ‘Durable DL110HTR’ at desired layer thickness when preparing your print file in Photocentric Studio
• Heat the resin to 30°C in the bottle
• Shake the resin bottle for 2 m

Post Processing

• Parts can be washed in 15 minutes using Photocentric Resin Cleaner or alternatively, in 10 minutes using Photocentric Resin Cleaner 30
• Once washed, rinse with warm water for 2 minutes
• Dry with compressed air to remove any remaining water. Or alternatively, leave to air-dry
• Place the platform into the Photocentric Cure L2 for
> > a minimum of 3 hours at 60°C for Durable DL110HW
> > a minimum of 4 hours at 60°C for Durable DL110HB
> > a minimum of 2 hours at 60°C for Durable DL110HTR
• For DL110HB & DL110HTR-Remove the platform from the Cure L2 and immediately submerge in cold water for thermal shocking. Parts can be removed from the platform with minimal effort
• For DL110HW- Remove the platform from the Cure L2 and allow it cool to room temperature. Remove the printed parts with the supplied scraper or the soft spatula
This product has no specific warranty. Bilby 3D will honor obligations under Australia Consumer Guarantee regulations if and where they apply to this product
Material Safety Data Sheet

Technical Data Sheet