CarbonX™ Carbon Fiber PA12 is made using high-modulus carbon fiber and a specialty Nylon 12 (PA12) that we chose for its printability, thermal properties, and chemical resistance. PA12 is widely used in a variety of industries due to its excellent chemical resistance, low moisture absorption, and wide processing window. This formulation ensures very low shrinkage in the printed part resulting in excellent dimensional stability. This makes CF-PA12 an excellent choice for tools, fixtures, and jigs.
Note: This filament is certified under Raise3Ds Open Filament Program, so a profile is available in the ideaMaker Library, ready to go.
Product Attributes Include:
- High thermal properties: 150°C HDT @ 0.45MPa [137°C HDT @ 1.8MPa]
- Excellent strength and stiffness over a wide temperature range - up to 150°C
- Continuous Use Temp (10,000 Hrs) of 120°C
- Very low moisture absorption = improved retention of mechanical properties after exposure to humidity
- Superior chemical resistance compared to PA6 type nylons
- Low shrink & warp = excellent dimensional stability
- Low density is ideal for light-weight parts - 1.16g/cc
Next >
More Information
Related Products:
Buy Now
Raise3D Premium PVA PLUS Support Material - 1.75mm - Natural - 750g
Raise3D Premium PVA+ is a polyvinyl alcohol (PVA)-based cold water-soluble support filament for FFF 3D printing with dual extruders.
*Note- Not detectable In optical filament sensors as on Raise 3d Printers
Buy Now
3DXTech CarbonX PEEK + 10 Carbon Fibre - 1.75mm - Black - 500g
Carbon Fiber reinforced PEEK 3D Printing Filament is ideal for the most demanding applications
Buy Now
Spectrum Nylon, PA6 Carbon Fibre, 1.75mm, 500g - UNTIL SOLD OUT
High temperature construction material
Nylon PA6 CF15 is a high-temperature, black, PA6-based construction material. Filling with 15% carbon fibres increases significantly the mechanical strength of the polyamide the material is based on. The filaments specific quality is the moisture absorption reduced by half and the water absorption time is four times lower than that of the pure PA6. Printing does not require a heated chamber and no deformation occurs. The material is compatible with the HIPS and BVOH support materials. In addition, Nylon PA6 CF15 features a very low linear shrinkage (up to 0.1%), a high deformation temperature (240°C), working temperature (180°C) and low thermal expansion coefficient (0.4 10-5/K).
Buy Now
PolyMaker Carbon Fibre reinforced PA6 Nylon, Black, 1.75mm, 2kg
PolyMide™ PA6-CF is a carbon fiber reinforced nylon (PA6) 3D printing material offering the highest strength, impact resistance and heat deflection of all Polymaker 3D printing materials.
Buy Now
Kimya ABS + Kevlar Fibre - 1.75mm - Black - 500g Spool
ABS KEVLAR has been deisgned for 3D printing by a precise formulation of aramid fibers into ABS materials.
Buy Now
3DXTech High-Temp Nylon + Carbon Fibre - 1.75mm - Black - 750g
CarbonX™ CF-HTN is an advanced semi-aromatic polyphthalamide (PPA) reinforced with high-modulus carbon fiber. This polymer is widely used for metal replacement applications that must resist high mechanical loads at elevated temperatures and aggressive chemical environments. HTN has traditionally been a go-to material for demanding applications in automotive, aerospace, oil & gas, electrical, electronics, and industrial markets.
Buy Now
3DXTech CarbonX PEEK + 20 Carbon Fibre - 1.75mm - Black - 500g
Carbon Fiber reinforced PEEK 3D Printing Filament is ideal for the most demanding applications
Buy Now
Kimya ABS + Carbon Fibre - 1.75mm - Black - 500g Spool
ABS CARBON FILAMENT improves interlayer adhesion and increases compression strength.
Buy Now
PolyMaker Carbon Fibre Reinforced PA6+12 Nylon, 1.75mm, 500g
PolyMide™ PA612-CF is a carbon fiber reinforced nylon filament based on a copolymer of Nylon 6 and Nylon 12. Featuring 15% chopped carbon fibers by weight, this filament has lower moisture sensitivity compared to PA6/66 and PA6-based materials, and better mechanical properties than PA12-based materials.
Buy Now
PolyMaker Carbon Fibre reinforced PA6 Nylon, Black, 1.75mm, 500g
PolyMide™ PA6-CF is a carbon fiber reinforced nylon (PA6) 3D printing material offering the highest strength, impact resistance and heat deflection of all Polymaker 3D printing materials.
Copyright 2011-2024 Bilby3D Pty. Ltd.
Sydney - Kingsgrove, NSW
Melbourne - Clayton, VIC
Perth - Belmont, WA
3D Printers
Bilby 3D Technical Support
3D Printer Service and Repair
Courses and Training
Materials / Filament
3D Scanners
Parts and Spares
Tools & Jigs